CC3-105  

 

 

Unfilled, Low Viscosity, General Purpose Potting Resin

 

 

CC3-105 exhibits a wide variety of excellent features found only in the highest quality epoxy resins. It is a

low viscosity, unfilled, resilient, transparent epoxy which can be cured at room temperature or with heat.

 

 

SUGGESTED APPLICATIONS:

 

Epoxy Glass Lamination:                               excellent wetting out properties

Thin Glue-Line Bonding:                                no bulky filler to occupy space

Void-Free, See Through Castings:                  low viscosity, air released rapidly

 

ELECTRICAL AND PHYSICAL PROPERTIES:    
    H-7 Hardener  Ancamine Z
  Specific Gravity @ 25’ C 1.1 1,2
  Viscosity @ 25’ C, cps  300 to 500 300 to 600
  Thermal Conductivity: BTU/ft2/hr/'F/in  1.4 1.4
  Flexural Strength: psi    9,000 10,500
  Izod Impact: ft lbs/in of notch   0.5 0.5
  Water Absorption: %, 7 days @ 25’ C 0.13 0.12
  Volume Resistivity @ 25’ C, ohm-cm

1013  1013 
  Dielectric Strength, volts/mil 380 390
  Bond Shear Strength: 1 in overlap 2,000 2,300
  Service Temperature, ‘C continuous  -55 to +150 -70 to +240
  Standard Color  Clear Amber

 

 

 

 

CHOICE OF HARDENERS:

 

            H-1 Hardener:                         Rigid, good dimensional stability, fast cure.

 

            H-7 Hardener:                         Resilient, excellent mechanical and thermal shock, low viscosity, good

                                                            air release, fast cure.

 

            Ancamine Z:                           Resilient, excellent mechanical and thermal shock, plus high heat

distortion, long pot life.

 

            H-10LV Hardener:                  Variable hardness, excellent impact properties, long pot life

 

 

 

 

 

 

 

CC3-105

 

 

HARDENER

PARTS BY WEIGHT
PER 100 PARTS OF RESIN

POT LIFE
100 GRAM
25'C (77'F)

CURE TIME
25' C
(77'F)

CURE TIME
65' C
(149' F)

CURE TIME
125 ' C
(257 ' F)

H-1 Hardener

14

30 mins.

6 hrs.

30 mins.

15 mins.

H-7 Hardener

29.0

45 mins.

24 hrs.

2 hrs.

30 mins.

Ancamine Z

18.0

4 hrs.

36 hrs.

16 hrs.

2 hrs.

H-10LV Hardener

__rigid _______ _-__33

3 hrs.

24 hrs.

3 hrs.

- - -

H-10LV Hardener

__semi-flex _____ __83

3 hrs.

24 hrs.

3 hrs.

- - -

H-10LV Hardener

__flexible ________133

3 hrs.

24 hrs.

3 hrs.

- - -

 

 

ROOM TEMPERATURE CURE:

 

H-1 Hardener:             Offers a working time of 30 minutes. Cures in 6 hours at 25’ C or 30 minutes at 65’ C.

                                    Produces a tough, rigid resin with good dimensional stability. Do not heat cure

                                    if the mass exceeds 100 grams.

 

H-7 Hardener:             Offers a working time of 45 minutes. Cures in 24 hours at 25’ C or 2 hours at 65’ C.

                                    Produces a tough, resilient resin with good mechanical and thermal shock properties.

 

H-10LV Hardener:      Offers a working time of 3 hours. Cures in 24 hours at 25’ C or 3 hours at 65’ C.

                                    Produces a variable hardness resin with excellent impact properties.

 

 

HEAT CURE:

 

Ancamine Z:               Offers a working time of 4 hours. Cures in 16 hours at 65’ C or 2 hours at 125’ C.

                                    Produces a tough, resilient resin with good mechanical and thermal shock properties

                                    plus a high heat distortion temperature of 125’ C.

 

MIXING INSTRUCTIONS:

 

Weigh out the desired amount of resin in a clean container. Add the hardener accurately by weight in the proper proportion as specified above. (ie. 14 grams of H-1 Hardener and 100 grams of CC3-105 for a total mix of 114 grams) Mix thoroughly. Use in a well ventilated area and avoid contact with eyes and skin.

   

 