CC3-105
|
|||
|
UNFILLED,
LOW VISCOSITY, GENERAL PURPOSE POTTING RESIN
|
|||
|
CC3-105 exhibits
a wide variety of excellent features found only in the highest quality
epoxy resins. It is a low viscosity, unfilled, resilient, transparent
epoxy which can be cured at room temperature or with heat.
|
|||
| SUGGESTED APPLICATIONS | |||
| Epoxy Glass Lamination: ___excellent wetting out properties. | |||
| Thin Glue-Line Bonding: ___no bulky filler to occupy space. | |||
| Void-Free, See Through Castings: ___medium viscosity, air released rapidly. | |||
| ELECTRICAL AND PHYSICAL PROPERTIES | H-7 | H-34 | |
| Specific Gravity: @ 25'C | 1.1 | 1.2 | |
| Viscosity: (centipoise) @ 25'C | 300-500 | 300-600 | |
Thermal Conductivity:
BTU/ft -hr-'F/in |
1.4 | 1.4 | |
| Flexural Strength: psi | 9,000 | 10,500 | |
| Izod Impact: ft. lbs / in of notch | .5 | .5 | |
| Water Absorption: 7 days @ 25'C, % | .13 | .12 | |
| Volume Resistivity: ohm-cm, @ 25'C | 10  |
10 |
|
| Dielectric Strength: volts/mil | 380 | 390 | |
| Bond Shear Strength: 1 in. overlap | 2,000 | 2,300 | |
| Service Temperature: 'C , continuous | -40 - +150 | -70 - +250 | |
| Standard Color | CLEAR | AMBER | |
CHOICE OF HARDENERS
| H-1 HARDENER | - rigid, good dimensional stability, fast cure. |
| H-7 HARDENER | - resilient, excellent mechanical and thermal shock, low viscosity, good air release, fast cure. |
| H-34 HARDENER | - resilient, excellent mechanical and thermal shock, plus high heat distortion, long pot life. |
| H-l0LV HARDENER | - variable hardness, excellent impact properties, long pot life. |
|
HARDENER
|
PARTS BY WEIGHT
PER 100 PARTS OF RESIN |
POT LIFE
100 GRAM 25'C (77'F) |
CURE TIME
25' C (77'F) |
CURE TIME
65' C (149' F) |
CURE TIME
125 ' C (257 ' F) |
|
H-1
|
14.0
|
30 mins.
|
6 hrs.
|
30 mins.
|
15 mins.
|
|
H-7
|
29.0
|
45 mins.
|
24 hrs.
|
2 hrs.
|
30 mins.
|
|
H-34
|
18.0
|
4 hrs.
|
36 hrs.
|
16 hrs.
|
2 hrs.
|
|
H- 10LV
|
__rigid _______
____-__33
|
3 hrs.
|
24 hrs.
|
3 hrs.
|
- - -
|
|
H-10LV
|
__semi-flex ___________83
|
3 hrs.
|
24 hrs.
|
3 hrs.
|
- - -
|
|
H-10LV
|
__flexible ____________133
|
3 hrs.
|
24 hrs.
|
3 hrs.
|
- - -
|
ROOM TEMPERATURE CURE
|
H-1 HARDENER |
-
|
Offers a working time of 30 mins. Cures in
6 hrs at 25'C or 30 mins at 65'C. Produces a tough, rigid resin with good dimensional stability. Do not heat cure if mass exceeds 200 grams. |
|
H-7 HARDENER
|
-
|
Offers a working time of 45 mins. Cures in
24 hrs at 25'C or 2 hrs at 65'C. Produces a tough, resilient resin with good mechanical and thermal shock properties. |
|
H-lOLV HARDENER |
- |
Offers a working time of 3 hrs at room temperature.
Cures overnight at room temperature or 3 hrs at 65'C. Do not heat cure if mass exceeds 300 grams. |
HEAT CURE
|
H-34 HARDENER
|
-
|
Offers a working time of 4 hrs at room temperature.
Cures in 2 hrs at 125'C. Produces a tough, resilient resin with good mechanical and thermal shock properties plus a high heat distortion temperature of 125'C. |
MIXING INSTRUCTIONS
Mix CC3-105 thoroughly in its shipping container to insure a
uniform consistency. Weigh out the
required amount of resin in a clean container. Add the hardener accurately by
weight in the proper
proportion as specified above. Mix thoroughly.
Use in a well ventilated area and avoid contact with eyes and skin.