CC3-402A
GENERAL PURPOSE, THERMALLY CONDUCTIVE
UL - 94V-0, FIRE RETARDANT, POTTING COMPOUND
CC3-402A is a general purpose, fire retardant epoxy potting resin exhibiting low abrasion resistance. It is designed to be used where low viscosity and good wetting-out properties are important. Low shrinkage and good thermal shock resistance minimize stress on potted components. A choice of hardeners enable CC3-402A to be cured either at room temperature or with heat.
Even though the entire CC3-402A series offers a low percent of filler separation, it is advisable to always mix the contents in the shipping container before using.
| ELECTRICAL AND PHYSICAL PROPERTIES | ||
| Specific Gravity: @ 25 ' C | 1.45 | |
| Viscosity: (centipoise) @ 25'C | 7,500 | |
Thermal Conductivity: BTU/ft -hr-'F/in |
8.0 | |
| Tensile Strength: psi @ 25'C | 7,200 | |
| Compressive Strength: psi @ 25 ' C | 22,700 | |
| Izod Impact: ft. lbs / in of notch | 0.8 | |
Coefficient of Thermal Expansion: in/in/'C
x 10 |
31 | |
| Heat Distortion: 'C | 65 | |
| Water Absorption: 7 days @ 25'C, % | 0.20 | |
| Volume Resistivity: ohm-cm, @ 25 ' C | 10 |
|
| Glass Transition Temperature (Tg, ' C) | 125 | |
| Dielectric Constant: 100 KC, @ 25 ' C | 4.2 | |
| Dissipation Factor: 100 KC, @ 25'C | 0.02 | |
| Dielectric Strength: volts/mil | 450 | |
| Linear Shrinkage: in/in | 0.004 | |
| Service Temperature: 'C, continuous | -55 to 155 | |
(Typical properties when cured with H-7)
CHOICE OF HARDENERS
| H-1 HARDENER |
- rigid, good dimensional stability, fast
cure. |
| H-7 HARDENER |
- resilient, excellent mechanical and thermal
shock, low viscosity, good air release, fast cure. |
| H-16 HARDENER |
- rigid, good low temperature, high humidity application,
fast cure. |
| H-34 HARDENER |
- resilient, excellent mechanical and thermal
shock, plus high heat distortion, long pot life. |
| H-lOLV HARDENER | - variable hardness, excellent impact properties, long pot life. |
|
HARDENER
|
PARTS BY WEIGHT
PER 100 PARTS OF RESIN |
POT LIFE
100 GRAM 25 ' C (77 ' F) |
CURE TIME
25 ' C (77 ' F) |
CURE TIME
65 ' C (149 ' F) |
CURE TIME
125 ' C (257 ' F) |
|
H-1
|
7.0
|
1 hrs.
|
24 hrs.
|
2 hrs.
|
---
|
|
H-7
|
14.5
|
2 hrs.
|
24 hrs.
|
2 hrs.
|
---
|
|
H-16
|
11
|
26 mins.
|
1 hr.
|
30 mins.
|
10 mins.
|
|
H-34
|
10.2
|
4 hrs.
|
---
|
16 hrs.
|
3 hrs.
|
|
H-10LV
|
resilient ______20
|
3 hrs.
|
24 hrs.
|
3 hrs.
|
---
|
|
H-10LV
|
semi-flex _____43
|
3 hrs.
|
24 hrs.
|
3 hrs.
|
---
|
|
H-10LV
|
flexible _______65
|
3 hrs.
|
24 hrs.
|
3 hrs.
|
---
|
ROOM TEMPERATURE CURE
| H-1 HARDENER |
- Cures overnight at room temperature or
2 hours at 65'C. Do not heat cure if the mass
exceeds 200 grams. |
| H-7 HARDENER |
- Cures overnight at room temperature or
2 hours at 65'C. |
|
H-1OLV HARDENER |
- Cures overnight at room temperature or 3 hours at
65'C. |
| H-16 HARDENER | - Cures within 1 hour at room temperature or 30 minutes at 65 ' C. Do not heat cure if the mass exceeds 100 grams. |
HEAT CURE
| H-34 HARDENER | - Cures over night at 65'C or 3 hours at 125'C. For the best physical and electrical properties, a slow cure for 16 hours at 65'C followed by a post cure for 3 hours at 125'C is recommended. |
MIXING INSTRUCTIONS
Mix CC3-402A thoroughly in its shipping container to insure a uniform consistency. Weigh out the required amount of resin in a clean container. Add the hardener accurately by weight in the proper proportion as specified above. Mix thoroughly.
Use in a well ventilated area and avoid contact with eyes and skin.